Sandwich Panels, Aluminum and Thermoplastics honeycombs and Foams

CLEARPET is a lightweight sandwich panel with a PET foam core and skins in a fi breglass impregnated with epoxy resin.

Sandwich panels Clearpet

CLEARPET is a lightweight sandwich panel with a PET foam core and skins in a fi breglass impregnated with epoxy resin. The sandwich panels made with foam cores allow to reduce the thickness of the stone slab, obtaining lighter but equally resistant tops and coatings. PET foam is almost white. This foam core glued to a clear fi breglass permits to create a light surface maintaining the visual characteristics of the panels. Pet core is completely made of recycled material.
 

 

 

  A - SKINS IN GLASS FIBRE FABRIC
  Fibra di vetro impregnata di resina
  epossidica 500gr/m2

 
  B - PET FOAM CORE
 

 

  TDS TO DOWNLOAD PDF

  ASK FOR QUOTATION

 
Clearpet
Сферы применения Легкие сэндвич-панели для наклеивания и армирования камня Легкие сэндвич-панели для наклеивания и армирования камня Backlight

 

ТЕХНИЧЕСКИЕ ХАРАКТЕРИСТИКИ

Technical data sheet for standard panels (dimensions, materials and special finishes on request)
TECHNICAL CHARACTERISTICS OF PANEL
panel thickness mm from 8 to 60
panel size mm
standard 1000x2500
other dimensions available on request
thickness’ tolerance mm
± 0,4
dimension’s tolerance mm
± 30
skins’ thickness mm
0,4
glass fibre skin type
Glass fibre Plain 500 gr/m² 600 tex
Impregnation
transparent epoxy resin with anti-UV filters
core materials
PET foam core
core thickness µm
from 7 to 60
diameter of honeycomb Ø = mm
from 3 to 19
core density Kg/m³
from 40 to 250 
adhesive two-component epoxy
PANEL PHYSICAL AND MECHANICAL PERFORMANCES
panel thickness mm
10
20
30
10
20
30
panel weight  Kg/m²
2,9±0,3
3,7±0,3
4,5±0,3
3,4±0,3
4,8±0,4
6,1±0,4
core material
PET foam core
 PET foam core

foam density

 80 135

compressive strength ASTM C 365-365 M  MPa

 0,83 2,3
shear modulus MPa

16

 35
yield load ASTM C 393† N

220

560

800

390

780

1400
deflection at yield load ASTM C 393† mm

16±2

11±1

7±1

26±2

14±2

10±1

skins E Elastic Modulus** Mpa

 28’000±1’000
moment of inertia I mm^4/m 18'400 76'000 174'000 18'400 76'000 174'000
middle resistance to peeling **  ASTM D1781 265 N/76mm - 17 Nm/m 300 N/76 mm - 23 Nm/m
thermal conductivity (referred to foam only)
a 23°C W/(m·°K)
0,034
0,037
thermal transmittance U (referred to foam only)
a 23°C  W/(m²·°K)
3,8
1,8
1,2
4,1
2,0
1,3
service temperature ** °C
- 40 / + 60

**     Tested by Internal Laboratory
***   Approximate value
†     Sample dimension with 4 support points (L, W) 540x50 mm

Disclaimer

Приведенные данные верны, насколько известно Cel Compenets srl, все предоставленные данные в цели информации продуктов компании Cel Compenets srl и их потенциального использования и возможные сферы приминения.Не даются и не подразумеваются никакие гарантии в отношении определенных свойств продуктов или их пригодности для конкретных приложений. CEL S.r.l. оставляет за собой право вносить изменения.